| Chemical Composition for Consumable Insert Wire | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ASME SFA 5.30 Group A Carbon Steel | ||||||||||||||
| Type | C | Mn | P | S | Si | Al* | Zr* | Ti* | ||||||
| MS1 | 0.06 | 1.00- 1.40 |
0.025 | 0.03 | 0.40- 0.60 |
0.05- 0.15 |
0.02- 0.12 |
0.05- 0.15 |
||||||
| MS2 | 0.20 | 0.90- 1.30 |
0.025 | 0.03 | 0.40- 0.65 |
|||||||||
| * Note: | Al + Zr+ Ti = 0.15 min. | |||||||||||||
| all listed elements are maximum unless specified | ||||||||||||||
| ASME SFA 5.30 Group B Chromium Molyedum Steel | ||||||||||||||
| Type | C | Mn | P | S | Si | Al | Cr | Mo | Cu | Ni | ||||
| 515 | 0.10 | 0.40- 0.70 |
0.03 | 0.03 | 0.40- 0.70 |
0.15 | 1.2- 1.5 |
0.40- 0.65 |
0.15 | |||||
| 521 | 0.10 | 0.40- 0.70 |
0.03 | 0.03 | 0.25 0.50 |
0.15 | 2.3- 2.7 |
0.90- 1.10 |
0.15 | 0.40 | ||||
| all listed elements are maximum unless specified | ||||||||||||||
| ASME SFA 5.30 Group C Austenitic Chromium Nickle Steel | ||||||||||||||
| Type | C | Cr | Ni | Mo | Cb + Ta | Mn | Si | P | S | Cr/Ni* | ||||
| 308 | 0.08 | 19.5- 22.0 |
9.0- 11.0 |
1.0- 2.5 |
0.25- 0.60 |
0.03 | 0.03 | 1.9/1 | ||||||
| 308L | 0.03 | 19.5- 22.0 |
9.0- 11.0 |
1.0- 2.5 |
0.25- 0.60 |
0.03 | 0.03 | 1.9/1 | ||||||
| 316 | 0.08 | 18.0- 20.0 |
11.0- 14.0 |
2.0- 3.0 |
1.0- 2.5 |
0.25- 0.60 |
0.03 | 0.03 | ||||||
| 316L | 0.03 | 18.0- 20.0 |
11.0- 14.0 |
2.0- 3.0 |
1.0- 2.5 |
0.25- 0.60 |
0.03 | 0.03 | ||||||
| 348 | 0.08 | 19.0- 21.5 |
9.0- 11.0 |
10 x C min.** to 1.0 Max. |
1.0- 2.5 |
0.25- 0.60 |
0.03 | 0.03 | 1.9/1 | |||||
| * Note | Chromium to Nickel Ratio (min.) | |||||||||||||
| ** Note | Tantalum content shall not exceed 0.10 percent | |||||||||||||
| all listed elements are maximum unless specified | ||||||||||||||
| ASME SFA 5.30 Group E Nickle Alloy Steel (includes Copper-Nickel) | ||||||||||||||
| Type | C | Mn | Fe | S | P | Si | Cu | Ni + Co | Al | Ti | Cr | Cb + Ta | Other | |
| 60 | 0.15 | 4.0 | 2.50 | 0.02 | 0.02 | 1.50 | Bal. | 32.0- 69.0 |
1.25 | 1.5- 3.0 |
0.50 | |||
| 61 | 0.15 | 1.0 | 1.0 | 0.01 | 0.03 | 0.75 | 0.25 | 93.0 min. | 1.50 | 2.0- 3.5 |
0.50 | |||
| 62 | 0.08 | 1.00 | 6.0- 8.0 |
0.015 | 0.03 | 0.35 | 0.50 | 70.0 min. | 14.0- 17.0 |
1.5- 3.0 |
1.0 | |||
| 67 | 0.04 | 1.0 | 0.4- 0.7 |
0.01 | 0.02 | 0.15 | Bal. | 29.0- 32.0 |
0.20- 0.50 |
0.50 | ||||
| 6A | 0.08 | 2.00- 2.75 |
8.0 | 0.15 | 0.30 | 0.35 | 0.50 | 67.0 min. | 2.5- 3.5 |
14.0- 17.0 |
0.50 | |||
| 82 | 0.10 | 2.50- 3.50 |
3.0 | 0.15 | 0.30 | 0.50 | 0.50 | 67.0 min. | 0.75 | 18.0- 22.0 |
2.0- 3.0 |
0.50 | ||
| all listed elements are maximum unless specified | ||||||||||||||